Ole auala ole gaosiga ole carbon fiber e faʻaaogaina le Dimethyl Sulfoxide(DMSO) e fai ma solvent, Acrylonitrile (AN) e pei o le monomer muamua, Itaconic Acid o le monomer lona lua, AIBN o le amataga lea e maua ai se kopi binary, ma le suauʻu susu. o le filifiliga pito i luga ua malilie i ai tagata tomai faapitoa carbon fiber.
Fa'amatalaga Fa'atekinolosi:
Leai. | Aitema | Vaega | Fa'amatalaga | Fa'amatalaga |
1 | Ole Density Linear | dtex | 1.15 | |
2 | Malosi fa'asa | CN/dtex | ≥4.0 | |
3 | Fa'aumiumi | % | 12±2 | |
4 | Dimethyl Sulfoxide(DMSO) mea | % | <0.03 | |
5 | Su'u Suauu | % | 0.5-0.1 | |
6 | Fa'ai'u Fua Fa'aletonu | % | <3 | |
7 | Toe Toe Susū | % | ≤1 | |
8 | Fa'aaliga | Leai se Filament Motu |
Fa'agasologa:
Sauniuniga Mea Mata —→ Faafefiloi Monomer —→ Copolymerization —→ Filtration Muamua —→ Aveese Monomer —→ Filtration Lona Lua —→ Faafefiloi Faafefiloi —→ Filtration Tertiary —→ Teuina —→ Defoam —→ Mivili —→ taele (Primary) —→ vili taele (Secondary) —→ vili taele (Tertiary) —→ Mama —→ Vevela Falolo —→ Suauu —→ Faamago —→ Ausa Fa'aloloa —→ Fa'a'avevela—→ Antistatic Treatment —→ Precursor Winding
Leai. | Aitema | Vaega | Fa'amatalaga | Fa'amatalaga |
1 | Ole Density Linear | dtex | 1.15 | |
2 | Malosi fa'asa | CN/dtex | ≥4.0 | |
3 | Fa'aumiumi | % | 12±2 | |
4 | Dimethyl Sulfoxide(DMSO) mea | % | <0.03 | |
5 | Su'u Suauu | % | 0.5-0.1 | |
6 | Fa'ai'u Fua Fa'aletonu | % | <3 | |
7 | Toe Toe Susū | % | ≤1 | |
8 | Fa'aaliga | Leai se Filament Motu |
Raw Sauniuniga Mea —→ Monomer Mixture —→ Copolymerization —→ Primary Filtration —→ Monomer Remotive —→ Secondary Filtration —→ Mixed Batch Neutralization —→ Tertiary Filtration —→ Storage —→ Defoam —→ Spinning —→ spin bath (Primary) —→ vili taele (Secondary) —→ vili taele (Tertiary) —→ Mama —→ Vevela Falolo —→ Suauu —→ Faamago —→ Ausa Fa'aloloa —→ Fa'a'avevela—→ Antistatic Treatment —→ Precursor Winding